Aropol M 650 TBR
Thixotropic
Pre-accelerated
LSE version (Low Styrene Emission)
Low styrene content
Easy lamination
Good air release/de-aeration
Low shrinkage
Aropol M 650 TBR is a DCPD laminating resin featuring low styrene emission combined with a low styrene content. This resin is thixotropic and pre-accelerated. Easy lamination and good air release, combined with low shrinkage and good surface aesthetics, are characteristic of Aropol M 650 TBR.
Application
Aropol M 650 TBR is suitable for all general composite applications and can be processed using hand lay-up and spray-up techniques. Aropol M 650 TBR has a curing system that allows a maximum layer thickness of 12 mm wet-on-wet without causing an excessively high peak exotherm. For thinner laminates (2–5 mm), a peroxide dosage of 1.5–2% MEKP-50 is recommended to achieve fast curing.
Liquid | Viscosity | 1100 - 1300 mPa.s (Brookfield - LV2, 12 rpm) |
|---|---|---|
180 - 200 mPa.s (cone & plate) | ||
Styrene content | 35.5-38.5% | |
Cured | HDT | 70°C |
Elongation at break | 2.1% |